Mohammad Hadi Yousefi; Mohamad Mehdi Zerafat; Majid Shokri Doodeji; Samad Sabbaghi
Abstract
The objective of this work is to investigate the effect of dip-coating parameters on the performance of Alumina-PDMS hybrid nanofiltration membranes for water desalination. Ceramic supports used in this work were prepared with a 340 nm average pore size and 34% total porosity. The aim is to determine ...
Read More
The objective of this work is to investigate the effect of dip-coating parameters on the performance of Alumina-PDMS hybrid nanofiltration membranes for water desalination. Ceramic supports used in this work were prepared with a 340 nm average pore size and 34% total porosity. The aim is to determine optimum conditions of dipping time, PDMS concentration, and withdrawal speed in order to achieve high rejection and flux values. Dip-coating parameters were considered as dipping time (60 - 120 s), withdrawal speed (5 - 15 mm/s) and PDMS concentration (10 - 20 wt. %). Hybrid membranes were characterized using FE-SEM and FTIR analysis techniques. Pure water flux and salt rejection were also measured to evaluate the rejection performance. Alumina-PDMS hybrid nanofiltration membranes fabricated with dipping time = 120 s, withdrawal speed = 15 mm/s and 10 wt. % PDMS exhibited the best performance giving 30.5% rejection for NaCl and 53.8% for Na2SO4.
Samad Sabbaghi; Fateme Doraghi
Abstract
In this study, considering the importance of protecting the environment and preventing the pollution caused by industrial plants, a nanocomposite each component thereof is capable of removing the desired combination to solve this problem has been produced. To achieve this goal, ZnO/SnO2nanocomposite ...
Read More
In this study, considering the importance of protecting the environment and preventing the pollution caused by industrial plants, a nanocomposite each component thereof is capable of removing the desired combination to solve this problem has been produced. To achieve this goal, ZnO/SnO2nanocomposite was synthesized using the co-precipitation method. The characterization of this nanocomposite was conducted by DLS, XRD, FTIR and SEM. The nanocomposite size was about 15nm. Several parameters such as the initial concentration of the wastewater, as well as the amount of catalyst and time were investigated. The reduction of the particle size due to an increase in the surface area of the nanocomposite increased the amount of decolorization. For all the performed experiments, the dye removal rate was 100% and the difference was to do with the time of the complete removal of methylene blue. A decrease in the concentration of methylene blue in the range of the tested concentrations reduced the decolorization, and by increasing the amount of nanocomposite in the range of the tested values, a decline in decolorization was observed.